shortens the drying period of Mipa PUR HS, OC and 2K-HS-clear paint CC 4 and C 420
Especially recommended at winter with low temperatures. Significantly improves through-drying at room temperature without reducing the dust-dust time. This does not affect the course negatively. Also leads by stove drying to a much quicker hardening.

Note: By using Mipa 2K-reactive additive in combination with Mipa 2K-HS-Hardener HS 25, the Mipa 2K-HS-Hardener HS 10 can be replaced or saved. Also the pot time is reduced (approx. 50%).

suitable for Mipa 2K-paints (OC / AC / PUR) and Mipa plastic resin paints.
Prevents crater formation and improves the course of overpainting traces of silicone, polish, wax and grease. Quantity adding: 2 or max. 5% on base coat or base coat after addition of hardener with 2K paint materials.

universal, matting agent
To reduce the gloss of Mipa 1K and 2K topcoats (PUR-, OC-, PUR HS, plastic resin-, Nitrokombi-, PVC-paints). Liquid, easy to stir. The matting effect depends on the color, so the evaluation is only possible after drying.
Note: Not usable in clear coats. Mipa Multi-Mat additions and mixing ratios (attention with 2K lacquers the mixing ratio with Mipa 2K hardeners changes depending on the amount added) see product data sheet.

additive to increase elasticity
Suitable for Mipa 2K-auto and 2K-vehicle paints (OC, AC, PUR) and Mipa 2K-clear coats, which are processed in a mixing ratio 2:1, and Mipa 2K-HS-Express clear coat CX 3. Necessary when painting deformable plastics.

Quantity added: master paint + 10 to 50% and Mipa 2K-HS-Express clear coat CX 3 up to 15%

additive for the adaptation of 2-component coatings to specific application areas or spraying equipment, addition 5%
Ensures an optimized coating result when applying Mipa 2K top coats, especially in roller and brush application, but also in airmix and airless application. The special active ingredient mixture effectively prevents the risk of foam formation and also significantly improves deaeration, flow and gloss of the top coat. However, should problems occur during application, the use of Mipa 2C System Additive PUA is recommended.

Texture additive to increase slip resistance, suitable for MIPA top coat "Protector Truckbedliner" (8.94 16 74/7)